煤气化飞灰用作水泥混合材的试验研究

doi:10.19698/j.cnki.1001-6171.20225085

下载:

PDF (4260KB)
输出: BibTeX | EndNote (RIS)

摘要

对比测试了煤气化飞灰与粉煤灰的化学成分和微观形貌、不同比例煤气化飞灰替代粉煤灰作为水泥混合材的粉体流动性，及其作水泥混合材对水泥物理化学性能的影响。分析显示，与粉煤灰相比，煤气化飞灰具有比表面积大、玻璃微珠含量高、微珠球形度高等特性；替代粉煤灰作水泥混合材时，水泥胶砂流动性、强度均提高，需水量下降，可以替代粉煤灰用作水泥混合材。

	服务
	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	（）
	作者相关文章
	毛凯
	苏思思
	刘晓婕
	高鹏
	王嘉威

关键词: 煤气化飞灰水泥混合材玻璃微珠粘附效应

Abstract: The chemical composition and micro morphology of coal gasification fly ash and fly ash, the fluidity of fly ash with different proportions of coal gasification fly ash replacing fly ash, and the effect of coal gasification fly ash as cement admixture on the physical and chemical properties of cement were tested. The test results show that compared with fly ash, coal gasification fly ash has the characteristics of large specific surface area, high content of glass beads and high sphericity of beads; Instead of fly ash as admixture, the fluidity and strength of cement mortar are improved, and the water demand is decreased. The above results show that coal gasification fly ash can replace fly ash as cement admixture.

Key words: coal gasification fly ash cement admixture glass beads adhesion effect

收稿日期: 2021-12-25 修回日期: 2022-09-25 出版日期: 2022-09-25 发布日期: 2022-09-25 整期出版日期: 2022-09-25

ZTFLH:

TQ172.44

引用本文:

毛凯, 苏思思, 刘晓婕, 高鹏, 王嘉威. 煤气化飞灰用作水泥混合材的试验研究[J]. 水泥技术, 2022, 1(5): 85-90.
MAO Kai, Su Sisi, LIU Xiaojie, GAO Peng, WANG Jiawei. Experimental Study on Coal Gasification Fly Ash as Cement Admixture. Cement Technology, 2022, 1(5): 85-90.

链接本文:

http://www.cemteck.com/CN/10.19698/j.cnki.1001-6171.20225085 或 http://www.cemteck.com/CN/Y2022/V1/I5/85

[1]	. Review and Prospect of Engineering Practice of Waste Disposal in Cement Kiln in China[J]. Cement Technology, 2018, 1(1): 17 -21 .
[2]	DI Dongren, TAO Congxi, CHAI Xingteng. Revision of Cement Energy Consumption Standards and Energy Saving Technology(Ⅰ)[J]. Cement Technology, 2018, 1(1): 22 -26 .
[3]	LIU Yonggang, GAO Hongwei, XIAO Guiqing. Design Method of Road Structure Using Lean Concrete Base[J]. Cement Technology, 2018, 1(1): 27 -31 .
[4]	LIU Xu, LI Liang. Investigation of New Medium Temperature Wear-resistant Alloy Steel[J]. Cement Technology, 2018, 1(1): 32 -34 .
[5]	MA Debao. Finite Element Analysis of Inverted Cone in Raw Meal Silo[J]. Cement Technology, 2018, 1(1): 35 -38 .
[6]	HAN Zhongqi. [J]. Cement Technology, 2018, 1(1): 38 -48 .
[7]	XIE Jianzhong, LIAN Xuewen. Analysis and Solution of Segregation of the Kiln Ash in Continuous Raw Meal Homogenization Silo#br#[J]. Cement Technology, 2018, 1(1): 49 -53 .
[8]	GUAN Laiqing, HE Yongxian. [J]. Cement Technology, 2018, 1(1): 54 -59 .
[9]	WEI Can, ZHANG Yuanyuan, AI Jun. Application of Cement Intelligent Control System in Overseas Projects[J]. Cement Technology, 2018, 1(1): 60 -64 .
[10]	JIN Shuang. [J]. Cement Technology, 2018, 1(1): 72 -73 .