一种矾土尾矿渣作水泥混合材的试验研究
济南大学材料科学与工程学院
Experimental  Study  on  Bauxite  Tailings  as  Cement  Admixture
College of Material Science and Engineering, Jinan University
下载:  PDF (2157KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 本文探讨了一种矾土尾矿渣作为混合材对水泥性能的影响。分析了矾土尾矿渣的矿物及颗粒组成,测定了尾矿渣水泥的标准稠度需水量、凝结时间、强度等性能。结果表明:矾土尾矿渣主要含有高岭石类(多水高岭石、珍珠陶土、地开石等)、一水铝石和云母类(白云母、钾云母、多硅锂云母等)等矿物。经煅烧处理的尾矿渣用作混合材,水泥的标准稠度需水量偏高,凝结时间明显缩短,抗压强度稍低于矿渣微粉而高于粉煤灰;煅烧处理的尾矿渣与矿渣微粉、粉煤灰复掺,有助于降低需水量及提高水泥强度。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
吴长亮
李艳君
李大伟
刘晓存
关键词:  矾土尾矿渣  硅酸盐水泥  水泥混合材  性能    
Abstract: Effect of cement properties which using a bauxite tailings as admixture was studied. The mineral composition and the particle size distribution of the bauxite tailings were analyzed. The water demand at standard consistency, setting time and compressive strength of the bauxite tailings cement were tested. The results showed that: the original bauxite tailings contain the minerals of a class of kaolinite (halloysite, nacrite, dickite), diaspore and a class of mica (muscovite, potassium mica, polylithionite). Taking the burned bauxite tailings as admixture, the cement standard consistency was higher, the setting time was shortened obviously and the compressive strengths were a little lower than which with the fine blast furnace slag but higher than the fly ash. The burned bauxite tailings and fine blastfurnace slag and fly ash compositing together as admixture, the standard consistency was apt to decrease and the compressive strength increased.
Key words:  bauxite tailings    portland cement    cement admixture    properties
收稿日期:  2016-08-26                出版日期:  2017-03-25      发布日期:  2018-05-03      整期出版日期:  2017-03-25
TQ172.44  
引用本文:    
吴长亮, 李艳君, 李大伟, 刘晓存. 一种矾土尾矿渣作水泥混合材的试验研究[J]. 水泥技术, 2017, 1(2): 29-34.
WU Changliang, LI Yanjun, LI Dawei, LIU Xiaocun. Experimental  Study  on  Bauxite  Tailings  as  Cement  Admixture. Cement Technology, 2017, 1(2): 29-34.
链接本文:  
http://www.cemteck.com/CN/  或          http://www.cemteck.com/CN/Y2017/V1/I2/29
[1] 王庆江. 圆形钢管混凝土柱框架典型节点受力性能分析[J]. 水泥技术, 2018, 1(1): 83-88.
[2] 吴秋生, 姚丕强, 俞为民, 韩辉, 谈永泉, 范志勇, 于智军, 黄茜. 高性能贝利特硫铝酸盐水泥混凝土性能研究[J]. 水泥技术, 2017, 1(1): 19-24.
[1] . Review and Prospect of Engineering Practice of Waste Disposal in Cement Kiln in China[J]. Cement Technology, 2018, 1(1): 17 -21 .
[2] DI Dongren, TAO Congxi, CHAI Xingteng. Revision of Cement Energy Consumption Standards and Energy Saving Technology(Ⅰ)[J]. Cement Technology, 2018, 1(1): 22 -26 .
[3] LIU Yonggang, GAO Hongwei, XIAO Guiqing. Design Method of Road Structure Using Lean Concrete Base[J]. Cement Technology, 2018, 1(1): 27 -31 .
[4] LIU Xu, LI Liang. Investigation of New Medium Temperature Wear-resistant Alloy Steel[J]. Cement Technology, 2018, 1(1): 32 -34 .
[5] MA Debao. Finite Element Analysis of Inverted Cone in Raw Meal Silo[J]. Cement Technology, 2018, 1(1): 35 -38 .
[6] HAN Zhongqi. [J]. Cement Technology, 2018, 1(1): 38 -48 .
[7] XIE Jianzhong, LIAN Xuewen. Analysis and Solution of Segregation of the Kiln Ash in Continuous Raw Meal Homogenization Silo#br#[J]. Cement Technology, 2018, 1(1): 49 -53 .
[8] WEI Can, ZHANG Yuanyuan, AI Jun. Application of Cement Intelligent Control System in Overseas Projects[J]. Cement Technology, 2018, 1(1): 60 -64 .
[9] JIN Shuang. [J]. Cement Technology, 2018, 1(1): 72 -73 .
[10] ZHANG Jiangtao, LIU Baoliang. Processing of the Wet Materials of the Winter Cement Factory in the High Cold Region[J]. Cement Technology, 2018, 1(1): 74 -82 .
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
    PDF Preview