利用煤矸石和矿山剥离粘土生产低碱水泥的实践

doi:10.19698/j.cnki.1001-6171.20211081

下载:

PDF (1536KB)
输出: BibTeX | EndNote (RIS)

摘要分析了煤矸石和矿山剥离粘土的化学成分。采用煤矸石和矿山剥离粘土作硅铝质校正材料进行了生料配料及易烧性试验，确定了生产低碱水泥的配料方案。生产的熟料碱含量稳定在0.4%左右，生产的低碱水泥碱含量稳定在0.5%左右，水泥混合材掺加量提高至16%左右，既利用了废渣，又解决了矿山剥离粘土堆放的难题。

	服务
	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	（）
	作者相关文章
	孔德高
	徐梅花

关键词: 煤矸石矿山剥离粘土低碱水泥

Abstract: The chemical composition of coal gangue and clay stripped from mine was analyzed. The coal gangue and clay stripped from mine were used as silica-alumina correction materials for raw meal proportioning and burnability test, and the proportioning scheme for producing low alkali cement was determined. The alkali content of clinker produced is stable at about 0.4%, the alkali content of low-alkali cement produced is stable at about 0.5%, and the addition amount of cement mixture is increased to about 16%, which not only utilizes waste residue, but also solves the problem of stacking stripped clay in mines.

Key words: coal gangue mining stripping clay low alkali cement

收稿日期: 2020-07-11 出版日期: 2021-01-25 发布日期: 2021-02-04 整期出版日期: 2021-01-25

ZTFLH:

TQ172.44

引用本文:

孔德高, 徐梅花.

利用煤矸石和矿山剥离粘土生产低碱水泥的实践

[J]. 水泥技术, 2021, 1(1): 81-83.
KONG Degao, XU Meihua. Practice of Producing Low Alkali Cement with Coal Gangue and Mine Stripping Clay. Cement Technology, 2021, 1(1): 81-83.

链接本文:

http://www.cemteck.com/CN/10.19698/j.cnki.1001-6171.20211081 或 http://www.cemteck.com/CN/Y2021/V1/I1/81

[1]	王春梅, 杨立荣, 杨克锐, 张志勇. 旁路放风合并煤矸石脱水的工艺设想 [J]. 水泥技术, 2008, 1(4): 25-28.
[2]	王延斌. CPC循环流化床锅炉结渣问题的解决[J]. 水泥技术, 2006, 1(6): 61-63.
[3]	王中伟, 潘淑琴. 煤矸石部分替代粘土的配料应用 [J]. 水泥技术, 2006, 1(1): 87-88.
[4]	杨凤玲, 严生. 低温合成煤矸石水泥工艺参数的试验研究 [J]. 水泥技术, 2005, 1(5): 23-26.
[5]	王梅, 施惠生. 水泥－煤矸石复合胶凝体系的水化性能和微观结构初探 [J]. 水泥技术, 2005, 1(3): 32-35.
[6]	张永娟, 张雄. 煤矸石改善石灰石硅酸盐水泥耐蚀性的研究 [J]. 水泥技术, 2004, 1(4): 31-33.
[7]	张永娟, 张雄. 煤矸石颗粒群分布与煤矸石水泥活性的关系研究 [J]. 水泥技术, 2004, 1(1): 12-14.

[1]	. Review and Prospect of Engineering Practice of Waste Disposal in Cement Kiln in China[J]. Cement Technology, 2018, 1(1): 17 -21 .
[2]	DI Dongren, TAO Congxi, CHAI Xingteng. Revision of Cement Energy Consumption Standards and Energy Saving Technology(Ⅰ)[J]. Cement Technology, 2018, 1(1): 22 -26 .
[3]	LIU Yonggang, GAO Hongwei, XIAO Guiqing. Design Method of Road Structure Using Lean Concrete Base[J]. Cement Technology, 2018, 1(1): 27 -31 .
[4]	LIU Xu, LI Liang. Investigation of New Medium Temperature Wear-resistant Alloy Steel[J]. Cement Technology, 2018, 1(1): 32 -34 .
[5]	MA Debao. Finite Element Analysis of Inverted Cone in Raw Meal Silo[J]. Cement Technology, 2018, 1(1): 35 -38 .
[6]	HAN Zhongqi. [J]. Cement Technology, 2018, 1(1): 38 -48 .
[7]	XIE Jianzhong, LIAN Xuewen. Analysis and Solution of Segregation of the Kiln Ash in Continuous Raw Meal Homogenization Silo#br#[J]. Cement Technology, 2018, 1(1): 49 -53 .
[8]	GUAN Laiqing, HE Yongxian. [J]. Cement Technology, 2018, 1(1): 54 -59 .
[9]	WEI Can, ZHANG Yuanyuan, AI Jun. Application of Cement Intelligent Control System in Overseas Projects[J]. Cement Technology, 2018, 1(1): 60 -64 .
[10]	JIN Shuang. [J]. Cement Technology, 2018, 1(1): 72 -73 .