摘要通过调整原燃材料质量，加强水泥熟料生产过程控制，优化熟料配料方案，调整熟料生产工艺操作，熟料3d抗压强度由28.5MPa提高至31.0MPa，28d抗压强度由52.0MPa提高至57.0MPa，熟料配比由85%降至81%，水泥熟料质量得到改善，并取得了良好经济效益。

	服务
	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	（）
	作者相关文章
	黄强
	姜晓红
	袁仕
	刘战梅

关键词: 熟料质量原燃材料配料方案生产工艺

Abstract:

By adjusting the quality of raw and fuel materials, strengthening the control of cement clinker production process, optimizing the clinker batching plan, and adjusting the clinker production process operation, the 3d compressive strength of clinker was increased from 28.5MPa to 31.0MPa, and the 28d compressive strength was increased from 52.0MPa was increased to 57.0MPa, the proportion of clinker was reduced from 85% to 81%, the quality of cement clinker was improved, and good economic benefits were achieved.

Key words: clinker quality raw and fuel materials batching plan production process

收稿日期: 2021-11-20 修回日期: 2022-07-25 出版日期: 2022-07-25 发布日期: 2022-07-25 整期出版日期: 2022-07-25

ZTFLH:

TQ172.13

引用本文:

黄强, 姜晓红, 袁仕, 刘战梅. 提高水泥熟料强度的主要措施[J]. 水泥技术, 2022, 1(4): 76-78.
HUANG Qiang, JIANG Xiaohong, YUAN Shi, LIU Zhanmei. Main Measures to Improve the Strength of Cement Clinker. Cement Technology, 2022, 1(4): 76-78.

链接本文:

http://www.cemteck.com/CN/10.19698/j.cnki.1001-6171.20224076 或 http://www.cemteck.com/CN/Y2022/V1/I4/76

[1]	张林, 谭建春, 杨勇, 刘波. 道路硅酸盐水泥生产制备初探[J]. 水泥技术, 2022, 1(3): 84-87.
[2]	韦爱玲, 陈远胜, 梁乾. 高含量MgO原料对水泥熟料的不良影响及应对措施[J]. 水泥技术, 2021, 1(6): 54-60.
[3]	张同天. 提高机立窑熟料质量的途径[J]. 水泥技术, 2002, 1(3): 104-106.
[4]	刘祥. 砂岩代替部分粘土生产优质水泥[J]. 水泥技术, 2002, 1(1): 70-71.
[5]	杨基典. 实施水泥新标准促进水泥生产技术进步[J]. 水泥技术, 2001, 1(2): 22-24.

[1]	. Review and Prospect of Engineering Practice of Waste Disposal in Cement Kiln in China[J]. Cement Technology, 2018, 1(1): 17 -21 .
[2]	DI Dongren, TAO Congxi, CHAI Xingteng. Revision of Cement Energy Consumption Standards and Energy Saving Technology(Ⅰ)[J]. Cement Technology, 2018, 1(1): 22 -26 .
[3]	LIU Yonggang, GAO Hongwei, XIAO Guiqing. Design Method of Road Structure Using Lean Concrete Base[J]. Cement Technology, 2018, 1(1): 27 -31 .
[4]	LIU Xu, LI Liang. Investigation of New Medium Temperature Wear-resistant Alloy Steel[J]. Cement Technology, 2018, 1(1): 32 -34 .
[5]	MA Debao. Finite Element Analysis of Inverted Cone in Raw Meal Silo[J]. Cement Technology, 2018, 1(1): 35 -38 .
[6]	HAN Zhongqi. [J]. Cement Technology, 2018, 1(1): 38 -48 .
[7]	XIE Jianzhong, LIAN Xuewen. Analysis and Solution of Segregation of the Kiln Ash in Continuous Raw Meal Homogenization Silo#br#[J]. Cement Technology, 2018, 1(1): 49 -53 .
[8]	GUAN Laiqing, HE Yongxian. [J]. Cement Technology, 2018, 1(1): 54 -59 .
[9]	WEI Can, ZHANG Yuanyuan, AI Jun. Application of Cement Intelligent Control System in Overseas Projects[J]. Cement Technology, 2018, 1(1): 60 -64 .
[10]	JIN Shuang. [J]. Cement Technology, 2018, 1(1): 72 -73 .